Comparative Studies of g-C3N4 and C3N3S3 Organic Semiconductors-Synthesis, Properties, and Application in the Catalytic Oxygen Reduction.

Exfoliated g-C3N4 is a well-known semiconductor utilized in heterogenous photocatalysis and water splitting. An improvement in light harvesting and separation of photogenerated charge carriers may be obtained by polymer doping with sulfur. In this work, we incorporate sulfur into the polymer chain by chemical polymerization of trithiocyanuric acid (C3N3S3H3) to obtain C3N3S3. The XRD measurements and TEM images indicated that C3N3S3, in contrast to g-C3N4, does not exist in the form of a graphitic structure and is not exfoliated into thin lamellas. However, both polymers have similar optical properties and positions of the conduction and valence bands. The comparative studies of electrochemical oxygen reduction and hydrogen evolution indicated that the overpotentials for the two processes were smaller for C3N3S3 than for g-C3N4. The RDE experiments in the oxygen-saturated solutions of 0.1 M NaOH have shown that O2 is electrochemically reduced via the serial pathway with two electrons involved in the first step. The spectroscopic experiments using NBT demonstrated that both polymers reveal high activity in the photocatalytic reduction of oxygen to superoxide anion radical by the photogenerated electrons.

Enhanced Performance of Camphorsulfonic Acid-Doped Perovskite Solar Cells.

High-quality perovskite film with large grains and therefore reduced grain boundaries plays a significant role in improving the power conversion efficiency (PCE) and ensuring good long-term stability of the perovskite solar cells. In this work, we found that adding camphorsulfonic acid (CSA), a Lewis base, to the perovskite solution results in the crystallization of larger perovskite grains. By varying the concentration of CSA, we found that the optimal concentration of the additive is 1 mg/mL, which leads to an 20% increase in PCE of the cells compared to the reference CSA-free cell. Interestingly, we observed that the PCE of cells with an excess of CSA was initially poor, but may increase significantly over time, possibly due to CSA migration to the hole-transporting layer, leading to an improvement in its conductivity.